Anisotropy In Sheet Metals

Anisotropy in sheet metal can be useful in deep drawing and other forming processes.

Anisotropy in sheet metals.

For sheet metals the r values are normally determined for three different directions of loading in plane 0 degrees 45 degrees and 90 degrees to the rolling direction and denoted by r 0 r 45 and r 90 respectively and the normal or average r value r m or normal anisotropy is measured as follows. Due to their crystallographic structure and the characteristics of the rolling process sheet metals generally exhibit a significant anisotropy of mechanical properties. Narayanasamy b e m tech m engg ph d d sc professor department of production engineering national institute of technology tiruchirappalli 620 015 tamil nadu india. A method to include the distribution of strains in the identification of the planar anisotropy of sheet metals is proposed.

This paper reviews the most recent models for description of the anisotropic plastic behavior and formability of sheet metals. Yield locus for a biaxial plane stress condition the von. The type of plastic anisotropy usually desired in sheet metal forming is that the sheet is isotropic in the plane and. After a brief review of classic isotropic yield functions recent.

Anisotropy includes elastic and plastic anisotropy. During rolling the sheet develops anisotropy both in the plane of the sheet called planer anisotropy as well in the thickness of sheet called anisotropy ratio. The method includes the optical measurement of strains on a flat specimen with a varying cross section and an inverse parameter identification scheme which minimizes the differences between the numerical simulation results and the experimental measurements by using. Dr r narayanasamy anisotropy of sheet metals.

The planer anisotropy is responsible for development of ears on the cup. Anisotropy in sheet metals. A model for technology transfer mat. The variation of their plastic behavior with direction is assessed by a quantity called lankford parameter or anisotropy coefficient 4 1.